Ukwengeza u-35% we-glass fiber e-PA, izakhiwo zemishini, ukuqina kosayizi, ukumelana nokushisa kanye nokumelana nokuguga kwe-PA kwathuthukiswa kakhulu, futhi amandla okumelana nokukhathala ayephindwe izikhathi ezingu-2.5 kunalokho okungathuthukisiwe. okufana nalokho lapho kungathuthukisiwe, kodwa ngenxa yokuthi ukugeleza kubi kakhulu, ingcindezi yomjovo nesivinini somjovo kufanele kunyuswe ngokufanelekile, futhi izinga lokushisa lesilinda kufanele linyuswe ngo-10-40℃. inqubo yokubumba umjovo, okuholela ekusebenzeni komshini kanye nesilinganiso sokuncipha endaweni yokuma, okuholela ekuguqukeni nasekuguqukeni, ngakho-ke, ukwakheka kwesikhunta, isikhundla nokuma kwetheku lokuthulula kufanele kube okunengqondo, inqubo ingathuthukisa izinga lokushisa kwesikhunta, umkhiqizo ungafakwa emanzini ashisayo ukuze uphole kancane.Ngaphezu kwalokho, uma sikhulu ingxenye yokwengeza i-fiber yengilazi, i-pl iyaguga kakhulu.izakhi zokubumba ze-astic zomshini wokubumba umjovo, kungcono ukusebenzisa isikulufu se-bimetallic nesilinda.
Manje sinomunye wemishini yokukhiqiza ethuthuke kakhulu, onjiniyela abanolwazi nabaqeqeshiwe nabasebenzi, izinhlelo zokuphatha ikhwalithi ezithathwayo kanye neqembu elinobungane lokuthengisa lamakhono okusekelwa ngaphambi/ngemuva kokuthengisa kwe-New Arrival China Auto Parts 35% Fiberglass Reinforced Nylon 66 PA 66 Resin, “Dala Amanani, Ikhasimende Elisebenzelayo!”kungaba inhloso esiyiphishekelayo.Sithemba ngobuqotho ukuthi wonke amaklayenti azokwakha ukubambisana okuhlala isikhathi eside nokuphumelelayo nathi.Uma ufisa ukuthola amaqiniso engeziwe mayelana nebhizinisi lethu, Qiniseka ukuthi uthintana nathi manje.
Izakhiwo Zomzimba | Okujwayelekile | Iyunithi | Inani |
Incazelo | ISO 1043 | I-PA66-GF35 | |
Ukuminyana | ISO 1183 | kg/m3 | 1.41 |
Ukuncipha | ISO 2577,294-4 | % | 0.3-0.9 |
I-Melt Temperature (DSC) | ISO 11357-1/-3 | °C | 260 |
Izakhiwo Zemishini | |||
I-Tensile Modulus | ISO 527-1/-2 | I-MPa | 12000 |
Amandla Okuqina | ISO 527-1/-2 | I-MPa | 215 |
Elongation at Break | ISO 527-1/-2 | % | -> n |
I-Flexural Modulus | ISO 178 | I-MPa | 10000 |
Amandla e-Flexural | ISO 178 | I-MPa | 310 |
Amandla Omphumela We-Charpy Notched (23 °C) | ISO 179/leA | kJ/m2 | 15 |
Amandla Omthelela we-Charpy (23°C) | ISO 179/leU | kJ/m2 | 90 |
Izakhiwo ezishisayo | |||
Izinga Lokushisa Lokuguquguquka A (1.80 MPa) | ISO 75-1/-2 | °C | 250 |
Ukuvutha | |||
Ukuvutha | I-UL-94 | 1.6mm | HB |
Qaphela | I-fiber yengilazi iqinisiwe |